Reinforced poly(phenylene ether)-polysiloxane block copolymer composition, and article comprising same

ABSTRACT

A reinforced poly(phenylene ether)-polysiloxane block copolymer composition includes specific amounts of a poly(phenylene ether)-polysiloxane block copolymer reaction product, a flame retardant, and a reinforcing filler. The composition exhibits a desirable balance of flame retardancy, heat resistance, and stiffness relative to a corresponding poly(phenylene ether) composition, and it is useful to fabricate articles including fuser holders for electrophotographic copiers.

CROSS-REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. Nonprovisional patent application Ser. No. 13/781,792, filed 1 Mar. 2013, which claims the benefit of U.S. Provisional Patent Application Nos. 61/741,785, filed 8 Nov. 2012, and 61/739,951, filed 20 Dec. 2012. These priority applications are fully incorporated herein by reference.

BACKGROUND OF THE INVENTION

Poly(phenylene ether) is a type of plastic known for its excellent water resistance, dimensional stability, and inherent flame retardancy. Properties such as strength, stiffness, chemical resistance, and heat resistance can be tailored by blending it with various other plastics in order to meet the requirements of a wide variety of consumer and industrial products, for example, plumbing fixtures, electrical boxes, automotive parts, and insulation for wire and cable.

Some applications for poly(phenylene ether)-based compositions require significant flame retardant capability. Examples include molded articles in the construction, transportation, electronics, and solar power industries. Poly(phenylene ether) is inherently flame retardant, but it is often blended with other components, such as impact modifiers and flow promoters, that reduce the flame retardancy of the resulting composition even as they improve its processing and mechanical properties. So, flame retardant additives are often required for blends of poly(phenylene ether)s with these other components.

Some molded articles require a flammability rating of V-0 in the 20 millimeter Vertical Burning Flame Test of Underwriter's Laboratory Bulletin 94 “Tests for Flammability of Plastic Materials, UL 94”. This V-0 rating can be difficult to achieve in a poly(phenylene ether) composition, even when flame retardant concentration is increased, and concentrations of flammable components are decreased. And when the V-0 rating is achievable, it often comes at the expense of diminished heat resistance and stiffness.

There remains a need for a poly(phenylene ether)-containing molding composition that exhibits a UL 94 V-0 rating while maintaining high heat resistance and stiffness.

BRIEF SUMMARY OF EMBODIMENTS OF THE INVENTION

One embodiment is a composition, comprising: 0.5 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; and 5 to 40 weight percent of a reinforcing filler; wherein all weight percents are based on the total weight of the composition.

Another embodiment is a composition, comprising: 0.5 to 5 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; 6 to 14 weight percent of a flame retardant comprising an organophosphate ester; 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and 15 to 25 weight percent of glass fibers; wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters; and wherein all weight percents are based on the total weight of the composition.

Another embodiment is an article comprising a composition, comprising: 0.5 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; and 5 to 40 weight percent of a reinforcing filler; wherein all weight percents are based on the total weight of the composition.

These and other embodiments are described in detail below.

DETAILED DESCRIPTION OF THE INVENTION

The present inventors have determined that the difficult-to-achieve property combination of a UL 94 V-0 rating, high heat resistance, and high stiffness is provided by a composition comprising 0.5 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; and 5 to 40 weight percent of a reinforcing filler; wherein all weight percents are based on the total weight of the composition. Specifically, the composition can exhibit a flammability rating of V-0 at a sample thickness less than or equal to 1.5 millimeters in the 20 millimeter Vertical Burning Flame Test of Underwriter's Laboratory Bulletin 94 “Tests for Flammability of Plastic Materials, UL 94”, a heat deflection temperature of at least 110° C. determined according to ASTM D 648-07 using a stress of 1.82 megapascals (MPa) and a sample thickness of 6.4 millimeters, a flexural modulus of at least 3,500 megapascals measured at 23° C. according to ASTM D 790-07e1 using a sample thickness of 6.4 millimeters. As demonstrated in the working examples below, in some embodiments the V-0 rating can be achieved at a thickness at least as low as 0.75 millimeters, the heat deflection temperature can be at least as high as 168° C., and the flexural modulus can be at least as high as 6,178 megapascals. In some embodiments, the composition exhibits the property combination of a UL 94 V-0 rating at a thickness of 1.5 millimeters, a heat deflection temperature of at least 150° C. determined according to ASTM D 648-07 using a stress of 1.82 megapascals (MPa) and a sample thickness of 6.4 millimeters, and a flexural modulus of at least 5,000 megapascals measured at 23° C. according to ASTM D 790-07e1 using a sample thickness of 6.4 millimeters.

In addition to being superior to compositions based on poly(phenylene ether) homopolymers, the present composition is superior to alternative materials used in applications requiring a UL 94 V-0 rating. For example, alternative glass-filled poly(ethylene terephthalate) compositions and glass-filled poly(butylene terephthalate) compositions often utilize halogenated flame retardants to achieve a V-0 rating, whereas the present composition does not require a halogenated flame retardant. The glass-filled polyester compositions, which are based on crystalline resins, also exhibit greater warpage (part distortion) than the present composition utilizing amorphous resin.

The composition comprises a poly(phenylene ether)-polysiloxane block copolymer reaction product which in turn comprises a poly(phenylene ether)-polysiloxane block copolymer and a poly(phenylene ether) (without an incorporated polysiloxane block). For brevity, the poly(phenylene ether)-polysiloxane block copolymer reaction product is sometimes referred to herein as the “reaction product”. The poly(phenylene ether)-polysiloxane block copolymer reaction product is synthesized by oxidative polymerization of a mixture of monohydric phenol and hydroxyaryl-terminated polysiloxane. This oxidative polymerization produces poly(phenylene ether)-polysiloxane block copolymer as the desired product and poly(phenylene ether) as a by-product. This poly(phenylene ether) present in the reaction product is sometimes referred to herein as the “first poly(phenylene ether)” to distinguish it from a “second poly(phenylene ether)” that is optionally present in the composition and not derived from the poly(phenylene ether)-polysiloxane block copolymer reaction product. It is difficult and unnecessary to separate the first poly(phenylene ether) from the poly(phenylene ether)-polysiloxane block copolymer. The poly(phenylene ether)-polysiloxane block copolymer can therefore be incorporated into the present composition as a “poly(phenylene ether)-polysiloxane block copolymer reaction product” that comprises both the first poly(phenylene ether) and the poly(phenylene ether)-polysiloxane block copolymer.

The poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block and a polysiloxane block. The poly(phenylene ether) block is a residue of the polymerization of the monohydric phenol. In some embodiments, the poly(phenylene ether) block comprises phenylene ether repeating units having the structure

wherein for each repeating unit, each Z¹ is independently unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that the hydrocarbyl group is not tertiary hydrocarbyl, C₁-C₁₂ hydrocarbylthio, or C₁-C₁₂ hydrocarbyloxy; and each Z² is independently hydrogen, unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that the hydrocarbyl group is not tertiary hydrocarbyl, C₁-C₁₂ hydrocarbylthio, or C₁-C₁₂ hydrocarbyloxy. In some embodiments, the poly(phenylene ether) block comprises 2,6-dimethyl-1,4-phenylene ether repeating units, that is, repeating units having the structure

2,3,6-trimethyl-1,4-phenylene ether repeating units, or a combination thereof.

The polysiloxane block is a residue of the hydroxyaryl-terminated polysiloxane. In some embodiments, the polysiloxane block comprises repeating units having the structure

wherein each occurrence of R¹ and R² is independently hydrogen or C₁-C₁₂ hydrocarbyl; and the polysiloxane block further comprises a terminal unit having the structure

wherein Y is hydrogen, C₁-C₁₂ hydrocarbyl, or C₁-C₁₂ hydrocarbyloxy, and wherein each occurrence of R³ and R⁴ is independently hydrogen or C₁-C₁₂ hydrocarbyl. In some embodiments, the polysiloxane repeating units comprise dimethylsiloxane (—Si(CH₃)₂O—) units. In some embodiments, the polysiloxane block has the structure

wherein n is, on average, 20 to 60.

In a very specific embodiment, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60.

The hydroxyaryl-terminated polysiloxane comprises at least one hydroxyaryl terminal group. In some embodiments, the hydroxyaryl-terminated polysiloxane has a single hydroxyaryl terminal group, in which case a poly(phenylene ether)-polysiloxane diblock copolymer is formed. In other embodiments, the hydroxyaryl-terminated polysiloxane has two hydroxyaryl terminal groups, in which case in which case poly(phenylene ether)-polysiloxane diblock copolymer and/or poly(phenylene ether)-polysiloxane-poly(phenylene ether) triblock copolymer are formed. It is also possible for the hydroxyaryl-terminated polysiloxane to have a branched structure that allows three or more hydroxyaryl terminal groups and the formation of corresponding branched block copolymers.

In some embodiments, the hydroxyaryl-terminated polysiloxane comprises, on average, 20 to 80 siloxane repeating units, specifically 25 to 70 siloxane repeating units, more specifically 30 to 60 siloxane repeating units, still more specifically 35 to 50 siloxane repeating units, yet more specifically 40 to 50 siloxane repeating units. The number of siloxane repeating units in the polysiloxane block is essentially unaffected by the copolymerization and isolation conditions, and it is therefore equivalent to the number of siloxane repeating units in the hydroxyaryl-terminated polysiloxane starting material. When not otherwise known, the average number of siloxane repeating units per hydroxyaryl-terminated polysiloxane molecule can be determined by nuclear magnetic resonance (NMR) methods that compare the intensities of signals associated with the siloxane repeating units to those associated with the hydroxyaryl terminal groups. For example, when the hydroxyaryl-terminated polysiloxane is a eugenol-capped polydimethylsiloxane, it is possible to determine the average number of siloxane repeating units by a proton nuclear magnetic resonance (¹H NMR) method in which integrals for the protons of the dimethylsiloxane resonance and the protons of the eugenol methoxy group are compared.

In some embodiments, the poly(phenylene ether)-polysiloxane block copolymer reaction product has a weight average molecular weight of at least 30,000 atomic mass units. For example, the reaction product can have a weight average molecular weight of 30,000 to 150,000 atomic mass units, specifically 35,000 to 120,000 atomic mass units, more specifically 40,000 to 90,000 atomic mass units, even more specifically 45,000 to 70,000 atomic mass units. In some embodiments, the poly(phenylene ether)-polysiloxane block copolymer reaction product has a number average molecular weight of 10,000 to 50,000 atomic mass units, specifically 10,000 to 30,000 atomic mass units, more specifically 14,000 to 24,000 atomic mass units.

In some embodiments, the poly(phenylene ether)-polysiloxane block copolymer reaction product has an intrinsic viscosity of at least 0.3 deciliter per gram, as measured by Ubbelohde viscometer at 25° C. in chloroform. In some embodiments, the intrinsic viscosity is 0.3 to 0.5 deciliter per gram, specifically 0.31 to 0.5 deciliter per gram, more specifically 0.35 to 0.47 deciliter per gram.

One indication of the efficiency with which the hydroxyaryl-terminated polysiloxane is incorporated into block copolymer is the low concentration of so-called poly(phenylene ether) “tail” groups in the reaction product. In a homopolymerization of 2,6-dimethylphenol, a large fraction of product molecules have a so-called head-to-tail structure in which the linear product molecule is terminated on one end by a 3,5-dimethyl-4-hydroxyphenyl “head” and on the other end by a 2,6-dimethylphenoxy “tail”. Thus, when the monohydric phenol consists of 2,6-dimethylphenol, the poly(phenylene ether) tail group has the structure

wherein the 3-, 4-, and 5-positions of the ring are substituted with hydrogen atoms (that is, the term “2,6-dimethylphenoxy” refers to a monovalent group and does not encompass divalent 2,6-dimethyl-1,4-phenylene ether groups). In a copolymerization of monohydric phenol with hydroxyaryl-terminated polysiloxane, incorporation of the hydroxyaryl-terminated polysiloxane into block copolymer will reduce the concentration of phenylene ether “tail” groups. Thus, in some embodiments, the monohydric phenol consists of 2,6-dimethylphenol, and the reaction product of comprises less than or equal to 0.4 weight percent, specifically 0.1 to 0.4 weight percent, of 2,6-dimethylphenoxy groups, based on the weight of the reaction product. The 2,6-dimethylphenoxy tail end groups are characteristic of poly(2,6-dimethyl-1,4-phenylene ether) homopolymer with a head-to-tail (hydroxy-monoterminated) structure in which the linear product molecule is terminated on one end by a 3,5-dimethyl-4-hydroxyphenyl “head” and on the other end by a 2,6-dimethylphenoxy “tail”. So, the low concentration of 2,6-dimethylphenoxy tail end groups is an indication that the reaction product comprises a reduced concentration of such monofunctional homopolymer and an increased concentration of the desired poly(phenylene ether)-polysiloxane block copolymer.

The poly(phenylene ether)-polysiloxane block copolymer reaction product can further include groups derived from a diphenoquinone, which is itself an oxidation product of the monohydric phenol. For example, when the monohydric phenol is 2,6-dimethylphenol, the diphenoquinone is 3,3′,5,5′-tetramethyl-4,4′-diphenoquinone. During the build phase of the copolymerization, the diphenoquinone is typically incorporated into the “tail” end of a head-to-tail poly(phenylene ether) as the corresponding biphenyl group. Through further reactions, the terminal biphenyl group can become an internal biphenyl group in the first poly(phenylene ether) chain. In some embodiments, the monohydric phenol consists of 2,6-dimethylphenol, and the reaction product comprises 0.1 to 2.0 weight percent, and specifically 1.1 to 2.0 weight percent, of 2,6-dimethyl-4-(3,5-dimethyl-4-hydroxyphenyl)-phenoxy (“biphenyl”) groups. The biphenyl groups are present only in bifunctional (head-to-head or hydroxyl-diterminated) structure. So, the low concentration of biphenyl group is an indication that the reaction product comprises a reduced concentration of such bifunctional homopolymer and an increased concentration of the desired poly(phenylene ether)-polysiloxane block copolymer.

The oxidative copolymerization can be conducted with a reaction time greater than or equal to 110 minutes. The reaction time is the elapsed time between initiation and termination of oxygen flow. (Although, for brevity, the description herein repeatedly refers to “oxygen” or “oxygen flow”, it will be understood that any oxygen-containing gas, including air, can be used as the oxygen source.) In some embodiments, the reaction time is 110 to 300 minutes, specifically 140 to 250 minutes, more specifically 170 to 220 minutes.

The oxidative copolymerization can include a “build time”, which is the time between completion of monomer addition and termination of oxygen flow. In some embodiments, the reaction time comprises a build time of 80 to 160 minutes. In some embodiments, the reaction temperature during at least part of the build time can be 40 to 60° C., specifically 45 to 55° C.

The poly(phenylene ether)-polysiloxane block copolymer reaction product can be isolated from solution by an isolation procedure that minimizes volatile and nonvolatile contaminants. For example, in some embodiments the reaction product comprises less than or equal to 1 weight percent of total volatiles, specifically 0.2 to 1 weight percent of total volatiles. In some embodiments the monomer mixture is oxidatively copolymerized in the presence of a catalyst comprising a metal (such as copper or manganese), and the poly(phenylene ether)-polysiloxane block copolymer reaction product comprises less than or equal to 100 parts per million by weight of the metal, specifically 5 to 100 parts per million by weight of the metal, more specifically 10 to 50 parts per million by weight of the metal, even more specifically 20 to 50 parts by weight of the metal, based on the weight of the poly(phenylene ether)-polysiloxane block copolymer reaction product.

Certain isolation procedures make it possible to assure that the poly(phenylene ether)-polysiloxane block copolymer reaction product is essentially free of residual hydroxyaryl-terminated polysiloxane starting material. In other words, these isolation procedures assure that the polysiloxane content of the reaction product consists essentially of the polysiloxane blocks of poly(phenylene ether)-polysiloxane block copolymer. After termination of the copolymerization reaction, the poly(phenylene ether)-polysiloxane block copolymer reaction product can be isolated from solution using methods known in the art for isolating poly(phenylene ether)s from solution. For example, the poly(phenylene ether)-polysiloxane block copolymer reaction product can be isolated by precipitation with an antisolvent comprising at least 50 weight percent of one or more C₁-C₆ alkanols, such as methanol, ethanol, n-propanol, or isopropanol. The use of an isopropanol-containing antisolvent is advantageous because isopropanol is a good solvent for unreacted hydroxyaryl-terminated polysiloxane. Therefore, precipitation and/or washing with an isopropanol-containing antisolvent (e.g., isopropanol alone) substantially remove hydroxyaryl-terminated polysiloxane from the isolated product.

Using these methods, it is possible to produce a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising less than or equal to 1.5 weight percent of the hydroxyaryl-terminated polysiloxane, specifically less than or equal to 1 weight percent of the hydroxyaryl-terminated polysiloxane, more specifically less than or equal to 0.5 weight percent of the hydroxyaryl-terminated polysiloxane, still more specifically less than or equal to 0.1 weight percent of the hydroxyaryl-terminated polysiloxane, based on the total weight of the poly(phenylene ether)-polysiloxane block copolymer reaction product.

The composition comprises less than or equal to 10 parts by weight of hydroxyaryl-terminated polysiloxane not covalently bound in the poly(phenylene ether)-polysiloxane block copolymer for each 100 parts by weight of hydroxyaryl-terminated polysiloxane covalently bound in the poly(phenylene ether)-polysiloxane block copolymer. Within this limit, the amount of hydroxyaryl-terminated polysiloxane not covalently bound in the poly(phenylene ether)-polysiloxane block copolymer can be less than or equal to 5 parts by weight, specifically less than or equal to 3 parts by weight, more specifically less than or equal to 2 parts by weight, even more specifically less than or equal to 1 part by weight. In some embodiments, the composition comprises less than or equal to 0.1 weight percent of polysiloxane not covalently bound in the poly(phenylene ether)-polysiloxane block copolymer.

In some embodiments, the poly(phenylene ether)-polysiloxane block copolymer reaction product incorporates greater than 75 weight percent, of the hydroxyaryl-terminated polysiloxane starting material into the poly(phenylene ether)-polysiloxane block copolymer. Specifically, the amount of the hydroxyaryl-terminated polysiloxane incorporated into the poly(phenylene ether)-polysiloxane block copolymer can be at least 80 weight percent, more specifically at least 85 weight percent, still more specifically at least 90 weight percent, yet more specifically at least 95 weight percent.

Additional details relating to the preparation, characterization, and properties of the poly(phenylene ether)-polysiloxane block copolymer reaction product can be found in U.S. Pat. No. 8,017,697 to Carrillo et al., and in copending U.S. patent application Ser. No. 13/169,137 of Carrillo et al., filed Jun. 27, 2011.

In some embodiments, the composition comprises 0.025 to 5 weight percent of polysiloxane covalently bound in the poly(phenylene ether)-polysiloxane block copolymer. In other words, the poly(phenylene ether)-polysiloxane block copolymer contributes 0.025 to 5 weight percent of polysiloxane to the composition as a whole. In some embodiments, the covalently bound polysiloxane amount is 0.025 to 1 weight percent, specifically 0.025 to 0.5 weight percent, based on the total weight of the composition. In some embodiments, such as, for example, when the poly(phenylene ether)-polysiloxane block copolymer reaction product is purified via precipitation in isopropanol, the polysiloxane content of the composition consists essentially of polysiloxane that has been incorporated into the poly(phenylene ether)-polysiloxane block copolymer. In some embodiments, the reaction product comprises 1 to 8 weight percent siloxane repeating units and 12 to 99 weight percent phenylene ether repeating units, based on the total weight of the reaction product. Within these ranges, the amount of siloxane repeating units can be 2 to 7 weight percent, specifically 3 to 6 weight percent, more specifically 4 to 5 weight percent; and the amount of phenylene ether repeating units can be 93 to 98 weight percent, specifically 94 to 97 weight percent, more specifically 95 to 96 weight percent. The reaction product can include relatively small amounts of very low molecular weight species. Thus, in some embodiments, the reaction product comprises less than 25 weight percent of molecules having a molecular weight less than 10,000 atomic mass units, specifically 5 to 25 weight percent of molecules having a molecular weight less than 10,000 atomic mass units, more specifically 7 to 21 weight percent of molecules having a molecular weight less than 10,000 atomic mass units. In some embodiments, the molecules having a molecular weight less than 10,000 atomic mass units comprise, on average, 5 to 10 weight percent siloxane repeating units, specifically 6 to 9 weight percent siloxane repeating units.

Similarly, the reaction product can also include relatively small amounts of very high molecular weight species. Thus, in some embodiments, the reaction product comprises less than 25 weight percent of molecules having a molecular weight greater than 100,000 atomic mass units, specifically 5 to 25 weight percent of molecules having a molecular weight greater than 100,000 atomic mass units, more specifically 7 to 23 weight percent of molecules having a molecular weight greater than 100,000 atomic mass units. In some embodiments, the molecules having a molecular weight greater than 100,000 atomic mass units comprise, on average, 3 to 6 weight percent siloxane repeating units, specifically 4 to 5 weight percent siloxane repeating units.

In a very specific procedure for preparing the poly(phenylene ether)-polysiloxane block copolymer reaction product, the monohydric phenol is 2,6-dimethylphenol; the hydroxyaryl-terminated polysiloxane is a eugenol-capped polydimethylsiloxane comprising 35 to 60 dimethylsiloxane units; the oxidative copolymerization is conducted with a reaction time of 170 to 220 minutes; and the hydroxyaryl-terminated polysiloxane constitutes 2 to 7 weight percent of the combined weight of the monohydric phenol and the hydroxyaryl-terminated polysiloxane.

The composition comprises 0.5 to 91 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product, based on the total weight of the composition. In some embodiments, the reaction product amount is 30 to 91 weight percent, specifically 55 to 85 weight percent, more specifically 60 to 80 weight percent, still more specifically 64 to 74 weight percent. In other embodiments, the reaction product amount is 52 to 80 weight percent, specifically 53 to 70 weight percent, more specifically 53 to 63 weight percent. In still other embodiments, the reaction product amount is 5 to 20 weight percent, specifically 5 to 15 weight percent, more specifically 7 to 13 weight percent. In yet other embodiments, the reaction product amount is 0.5 to 5 weight percent, specifically 1 to 3 weight percent.

In some embodiments, particularly those in which the amount of the poly(phenylene ether)-polysiloxane block copolymer reaction product is less than 50 weight percent, it can be beneficial to include a second poly(phenylene ether) in the composition. As used herein, the term “second poly(phenylene ether)” refers to a poly(phenylene ether) that is not derived from the poly(phenylene ether)-polysiloxane block copolymer reaction. The second poly(phenylene ether) can be chemically the same as or different from the first poly(phenylene ether). Suitable first and second poly(phenylene ether)s include those comprising repeating structural units having the formula

wherein each occurrence of Z¹ is independently halogen, unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that the hydrocarbyl group is not tertiary hydrocarbyl, C₁-C₁₂ hydrocarbylthio, C₁-C₁₂ hydrocarbyloxy, or C₂-C₁₂ halohydrocarbyloxy wherein at least two carbon atoms separate the halogen and oxygen atoms; and each occurrence of Z² is independently hydrogen, halogen, unsubstituted or substituted C₁-C₁₂ hydrocarbyl provided that the hydrocarbyl group is not tertiary hydrocarbyl, C₁-C₁₂ hydrocarbylthio, C₁-C₁₂ hydrocarbyloxy, or C₂-C₁₂ halohydrocarbyloxy wherein at least two carbon atoms separate the halogen and oxygen atoms. As used herein, the term “hydrocarbyl”, whether used by itself, or as a prefix, suffix, or fragment of another term, refers to a residue that contains only carbon and hydrogen. The residue can be aliphatic or aromatic, straight-chain, cyclic, bicyclic, branched, saturated, or unsaturated. It can also contain combinations of aliphatic, aromatic, straight chain, cyclic, bicyclic, branched, saturated, and unsaturated hydrocarbon moieties. However, when the hydrocarbyl residue is described as substituted, it may, optionally, contain heteroatoms over and above the carbon and hydrogen members of the substituent residue. Thus, when specifically described as substituted, the hydrocarbyl residue can also contain one or more carbonyl groups, amino groups, hydroxyl groups, or the like, or it can contain heteroatoms within the backbone of the hydrocarbyl residue. As one example, Z¹ can be a di-n-butylaminomethyl group formed by reaction of a terminal 3,5-dimethyl-1,4-phenyl group with the di-n-butylamine component of an oxidative polymerization catalyst.

In some embodiments, the second poly(phenylene ether) has an intrinsic viscosity of 0.2 to 1 deciliter per gram measured by Ubbelohde viscometer at 25° C. in chloroform. Within this range, the second poly(phenylene ether) intrinsic viscosity can be 0.2 to 0.5 deciliter per gram, specifically 0.2 to 0.4 deciliter per gram, still more specifically 0.25 to 0.35 deciliter per gram.

In some embodiments, the second poly(phenylene ether) comprises 2,6-dimethyl-1,4-phenylene ether units, 2,3,6-trimethyl-1,4-phenylene ether units, or a combination thereof. In some embodiments, the second poly(phenylene ether) comprises a poly(2,6-dimethyl-1,4-phenylene ether). In some embodiments, the second poly(phenylene ether) comprises a poly(2,6-dimethyl-1,4-phenylene ether) having an intrinsic viscosity of 0.2 to 0.4 deciliter per gram, specifically 0.25 to 0.35 deciliter per gram, measured by Ubbelohde viscometer at 25° C. in chloroform.

When present, the second poly(phenylene ether) can be used in an amount of 5 to 90.5 weight percent, specifically 20 to 80 weight percent, more specifically 50 to 70 weight percent, based on the total weight of the composition.

In addition to the poly(phenylene ether)-polysiloxane block copolymer reaction product and the optional second poly(phenylene ether), the composition comprises a flame retardant. The flame retardant comprises an organophosphate ester, a phosphazene, or a combination thereof.

In some embodiments, the flame retardant comprises or consists of an organophosphate ester. Exemplary organophosphate ester flame retardants include phosphate esters comprising phenyl groups, substituted phenyl groups, or a combination of phenyl groups and substituted phenyl groups, bis-aryl phosphate esters based upon resorcinol such as, for example, resorcinol bis(diphenyl phosphate), as well as those based upon bisphenols such as, for example, bisphenol A bis(diphenyl phosphate). In some embodiments, the organophosphate ester is selected from tris(alkylphenyl)phosphates (for example, CAS Reg. No. 89492-23-9 or CAS Reg. No. 78-33-1), resorcinol bis(diphenyl phosphate) (CAS Reg. No. 57583-54-7), bisphenol A bis(diphenyl phosphate) (CAS Reg. No. 181028-79-5), triphenyl phosphate (CAS Reg. No. 115-86-6), tris(isopropylphenyl)phosphates (for example, CAS Reg. No. 68937-41-7), and combinations thereof.

In some embodiments the organophosphate ester comprises or consists of a bis-aryl phosphate having the formula

wherein R is independently at each occurrence a C₁-C₁₂ alkylene group; R⁹ and R¹⁰ are independently at each occurrence a C₁-C₅ alkyl group; R⁵, R⁶, and R⁸ are independently a C₁-C₁₂ hydrocarbyl group; R⁷ is independently at each occurrence a C₁-C₁₂ hydrocarbyl group; n is 1 to 25; and s1 and s2 are independently an integer equal to 0, 1, or 2. In some embodiments OR⁵, OR⁶, OR⁷ and OR⁸ are independently derived from phenol, a monoalkylphenol, a dialkylphenol, or a trialkylphenol.

As readily appreciated by one of ordinary skill in the art, the bis-aryl phosphate is derived from a bisphenol. Exemplary bisphenols include 2,2-bis(4-hydroxyphenyl)propane (bisphenol A), 2,2-bis(4-hydroxy-3-methylphenyl)propane, bis(4-hydroxyphenyl)methane, bis(4-hydroxy-3,5-dimethylphenyl)methane and 1,1-bis(4-hydroxyphenyl)ethane. In some embodiments, the bisphenol comprises bisphenol A.

In some embodiments, the flame retardant comprises a phosphazene. A phosphazene is a compound comprising repeating units having the structure

wherein each occurrence of R¹⁹ is independently C₁-C₆ alkoxy, unsubstituted or substituted phenoxy, or unsubstituted or substituted naphthyloxy. When present, the substituents on the phenoxy or naphthyloxy groups can be, for example, C₁-C₆ alkyl, C₁-C₆ alkoxy, or phenyl.

In some embodiments, the phosphazene comprises a cyclic phosphazene having the structure

wherein R¹⁹ is defined above and a is 3 to 12, specifically 3 to 6. In some embodiments, a is 3 and each occurrence of R¹⁹ is unsubstituted phenoxy.

In some embodiments, the phosphazene comprises a linear polyphosphazene having the structure

wherein R¹⁹ is defined above; b is 3 to 1,000; A is —N═P(O)(R¹⁹) or —N═P(R¹⁹)₃; and B is —P(R¹⁹)₄ or —P(O)(R¹⁹)₂.

The phosphazene can be crosslinked with a phenylene group, a biphenylene group, or a group having the structure

wherein X is C₁-C₆ alkylidene, O, S, or SO₂.

A mixture of at least two of cyclic phosphazenes, linear polyphosphazenes, and crosslinked phosphazenes can be used. In some embodiments, the phosphazene comprises at last 80 weight percent cyclic phosphazenes, based on the weight of the phosphazene.

Methods for making phosphazenes are known, and phosphazenes are commercially available as, for example, RABITLE™ FP-100 and RABITLE™ FP-110 from Fushimi Pharmaceutical Co., Ltd., IDB-Poretar-201 from ID-Biochem, and SPB-100 from Otsuka Chemical Company.

The amount of the organophosphate ester, phosphazene, or combination thereof can be 1 to 25 weight percent, based on the total weight of the composition. In some embodiments, the amount of the organophosphate ester, phosphazene, or combination thereof is 4 to 15 weight percent, specifically 4 to 12 weight percent, more specifically 4 to 10 weight percent. In other embodiments, the amount of the organophosphate ester, phosphazene, or combination thereof is 10 to 25 weight percent, specifically 15 to 25 weight percent.

In addition to the organophosphate ester and/or phosphazene, the flame retardant can, optionally, further comprise a dialkylphosphinate salt. As used herein, the term “dialkylphosphinate salt” refers to a salt comprising at least one cation and at least one dialkylphosphinate anion. In some embodiments, the dialkylphosphinate salt has the formula

wherein R^(a) and R^(b) are each independently C₁-C₆ alkyl; M is calcium, magnesium, aluminum, zinc, ammonium, or hydrocarbyl-substituted ammonium; and d is 2 or 3. Examples of R^(a) and R^(b) include methyl, ethyl, n-propyl, isopropyl, n-butyl, tert-butyl, n-pentyl, and phenyl. In some embodiments, R^(a) and R^(b) are ethyl, M is aluminum, and d is 3 (that is, the dialkylphosphinate salt is aluminum tris(diethylphosphinate)).

In some embodiments, the dialkylphosphinate salt is in particulate form. The dialkylphosphinate salt particles can have a median particle diameter (D50) less than or equal to 40 micrometers, or, more specifically, a D50 less than or equal to 30 micrometers, or, even more specifically, a D50 less than or equal to 25 micrometers. Additionally, the dialkylphosphinate salt can be combined with a polymer, such as the poly(phenylene ether)-polysiloxane block copolymer reaction product, the second poly(phenylene ether), or combination thereof, to form a masterbatch. The dialkylphosphinate salt masterbatch comprises the dialkylphosphinate salt in an amount greater than is present in the thermoplastic composition. Employing a masterbatch for the addition of the dialkylphosphinate salt to the other components of the composition can facilitate addition and improve distribution of the dialkylphosphinate salt.

In some embodiments, the dialkylphosphinate salt is used in an amount of 1 to 5 weight percent, specifically 1 to 3 weight percent, based on the total weight of the composition. When the amount of the organophosphate ester, phosphazene, or combination thereof is less than 4 weight percent, then the amount of dialkylphosphinate salt is sufficient to make the total flame retardant amount at least 4 weight percent. In some embodiments the composition comprises less than or equal to 1 weight percent of dialkylphosphinate salt, based on the total weight of the composition. In some embodiments the composition excludes dialkylphosphinate salt.

The composition comprises 4 to 25 weight percent of the flame retardant, based on the total weight of the composition. In some embodiments, the flame retardant amount is 4 to 15 weight percent, specifically 4 to 12 weight percent, more specifically 4 to 10 weight percent. In other embodiments, the flame retardant amount is 10 to 25 weight percent, specifically 15 to 25 weight percent.

In addition to the poly(phenylene ether)-polysiloxane block copolymer reaction product, the optional second poly(phenylene ether), and the flame retardant, the composition comprises a reinforcing filler. Reinforcing fillers include, for example, glass fibers, carbon fibers, wollastonite, halloysite, clays, talcs, micas, glass flakes, solid glass beads, hollow glass beads, solid ceramic beads, hollow ceramic beads, and combinations thereof. In some embodiments, the reinforcing filler comprises or consists of glass fibers.

Suitable glass fibers include those based on E, A, C, ECR, R, S, D, and NE glasses, as well as quartz. In some embodiments, the glass fiber has a diameter of 2 to 30 micrometers, specifically 5 to 25 micrometers, more specifically 10 to 15 micrometers. In some embodiments, the length of the glass fibers before compounding is 2 to 7 millimeters, specifically 3 to 5 millimeters. Suitable glass fiber is commercially available from suppliers including, for example, Owens Corning, Nippon Electric Glass, PPG, and Johns Manville.

The reinforcing filler can, optionally, include an adhesion promoter to improve its compatibility with the poly(phenylene ether)-polysiloxane block copolymer reaction product. Adhesion promoters include chromium complexes, silanes, titanates, zircoaluminates, propylene maleic anhydride copolymers, reactive cellulose esters, and the like.

The reinforcing filler can be used in an amount of 5 to 40 weight percent, based on the total weight of the composition. In some embodiments, the reinforcing filler amount is 8 to 30 weight percent, specifically 15 to 25 weight percent. In other embodiments, the reinforcing filler amount is 10 to 30 weight percent, specifically 15 to 25 weight percent.

The composition can, optionally, further include an impact modifier. Impact modifiers include, for example, rubber-modified polystyrenes, unhydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, hydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, acrylate core-shell impact modifiers (e.g., those having a crosslinked poly(butyl acrylate) core and a grafted poly(methyl methacrylate) shell), and combinations thereof.

The impact modifier can include a rubber-modified polystyrene. Rubber-modified polystyrene comprises polystyrene and polybutadiene. Rubber-modified polystyrenes are sometimes referred to as “high-impact polystyrenes” or “HIPS”. In some embodiments, the rubber-modified polystyrene comprises 80 to 96 weight percent polystyrene, specifically 88 to 94 weight percent polystyrene; and 4 to 20 weight percent polybutadiene, specifically 6 to 12 weight percent polybutadiene, based on the weight of the rubber-modified polystyrene. Suitable rubber-modified polystyrenes are commercially available as, for example, HIPS3190 from SABIC Innovative Plastics.

The impact modifier can include an unhydrogenated block copolymer of an alkenyl aromatic compound and a conjugated diene. For brevity, this component is referred to as an “unhydrogenated block copolymer”. The unhydrogenated block copolymer can comprise 10 to 90 weight percent of poly(alkenyl aromatic) content and 90 to 10 weight percent of poly(conjugated diene) content, based on the weight of the unhydrogenated block copolymer. In some embodiments, the unhydrogenated block copolymer is a low poly(alkenyl aromatic content) unhydrogenated block copolymer in which the poly(alkenyl aromatic) content is 10 to less than 40 weight percent, specifically 20 to 35 weight percent, more specifically 25 to 35 weight percent, yet more specifically 30 to 35 weight percent, all based on the weight of the low poly(alkenyl aromatic) content unhydrogenated block copolymer. In other embodiments, the unhydrogenated block copolymer is a high poly(alkenyl aromatic) content unhydrogenated block copolymer in which the poly(alkenyl aromatic) content is 40 to 90 weight percent, specifically 50 to 80 weight percent, more specifically 60 to 70 weight percent, all based on the weight of the high poly(alkenyl aromatic) content unhydrogenated block copolymer.

In some embodiments, the unhydrogenated block copolymer has a weight average molecular weight of 40,000 to 400,000 atomic mass units. The number average molecular weight and the weight average molecular weight can be determined by gel permeation chromatography and based on comparison to polystyrene standards. In some embodiments, the unhydrogenated block copolymer has a weight average molecular weight of 200,000 to 400,000 atomic mass units, specifically 220,000 to 350,000 atomic mass units. In other embodiments, the unhydrogenated block copolymer has a weight average molecular weight of 40,000 to 200,000 atomic mass units, specifically 40,000 to 180,000 atomic mass units, more specifically 40,000 to 150,000 atomic mass units.

The alkenyl aromatic monomer used to prepare the unhydrogenated block copolymer can have the structure

wherein R¹¹ and R¹² each independently represent a hydrogen atom, a C₁-C₈ alkyl group, or a C₂-C₈ alkenyl group; R¹³ and R¹⁷ each independently represent a hydrogen atom, a C₁-C₈ alkyl group, a chlorine atom, or a bromine atom; and R¹⁴, R¹⁵, and R¹⁶ each independently represent a hydrogen atom, a C₁-C₈ alkyl group, or a C₂-C₈ alkenyl group, or R¹⁴ and R¹⁵ are taken together with the central aromatic ring to form a naphthyl group, or R¹⁵ and R¹⁶ are taken together with the central aromatic ring to form a naphthyl group. Specific alkenyl aromatic monomers include, for example, styrene, chlorostyrenes such as p-chlorostyrene, methylstyrenes such as alpha-methylstyrene and p-methylstyrene, and t-butylstyrenes such as 3-t-butylstyrene and 4-t-butylstyrene. In some embodiments, the alkenyl aromatic monomer is styrene.

The conjugated diene used to prepare the unhydrogenated block copolymer can be a C₄-C₂₀ conjugated diene. Suitable conjugated dienes include, for example, 1,3-butadiene, 2-methyl-1,3-butadiene, 2-chloro-1,3-butadiene, 2,3-dimethyl-1,3-butadiene, 1,3-pentadiene, 1,3-hexadiene, and combinations thereof. In some embodiments, the conjugated diene is 1,3-butadiene, 2-methyl-1,3-butadiene, or a combination thereof. In some embodiments, the conjugated diene consists of 1,3-butadiene.

The unhydrogenated block copolymer is a copolymer comprising (A) at least one block derived from an alkenyl aromatic compound and (B) at least one block derived from a conjugated diene. The arrangement of blocks (A) and (B) includes a linear structure, a grafted structure, and a radial teleblock structure with or without a branched chain. Linear block copolymers include tapered linear structures and non-tapered linear structures. In some embodiments, the unhydrogenated block copolymer has a tapered linear structure. In some embodiments, the unhydrogenated block copolymer has a non-tapered linear structure. In some embodiments, the unhydrogenated block copolymer comprises a (B) block that comprises random incorporation of alkenyl aromatic monomer. Linear block copolymer structures include diblock (A-B block), triblock (A-B-A block or B-A-B block), tetrablock (A-B-A-B block), and pentablock (A-B-A-B-A block or B-A-B-A-B block) structures as well as linear structures containing 6 or more blocks in total of (A) and (B), wherein the molecular weight of each (A) block can be the same as or different from that of other (A) blocks, and the molecular weight of each (B) block can be the same as or different from that of other (B) blocks. In some embodiments, the unhydrogenated block copolymer is a diblock copolymer, a triblock copolymer, or a combination thereof.

In some embodiments, the unhydrogenated block copolymer excludes the residue of monomers other than the alkenyl aromatic compound and the conjugated diene. In some embodiments, the unhydrogenated block copolymer consists of blocks derived from the alkenyl aromatic compound and the conjugated diene. It does not comprise grafts formed from these or any other monomers. It also consists of carbon and hydrogen atoms and therefore excludes heteroatoms.

In some embodiments, the unhydrogenated block copolymer includes the residue of one or more acid functionalizing agents, such as maleic anhydride.

In some embodiments, the unhydrogenated block copolymer comprises a polystyrene-polybutadiene-polystyrene triblock copolymer. In some embodiments, the unhydrogenated block copolymer comprises a polystyrene-polyisoprene-polystyrene triblock copolymer.

Methods for preparing unhydrogenated block copolymers are known in the art and unhydrogenated block copolymers are commercially available. Illustrative commercially available unhydrogenated block copolymers include the polystyrene-polybutadiene-polystyrene triblock copolymers from Kraton Performance Polymers Inc. under the trade names Kraton™ D1101 and D1102; and the styrene-butadiene radial teleblock copolymers from Chevron Phillips Chemical Company under the trade names K-RESIN™ KK38, KR01, KR03, and KR05.

The impact modifier can be a hydrogenated block copolymer of an alkenyl aromatic compound and a conjugated diene. For brevity, this component is referred to as a “hydrogenated block copolymer”. The hydrogenated block copolymer is the same as the unhydrogenated block copolymer, except that in the hydrogenated block copolymer the aliphatic unsaturated group content in the block (B) derived from a conjugated diene has been at least partially reduced by hydrogenation. In some embodiments, the aliphatic unsaturation in the (B) block is reduced by at least 50 percent, specifically at least 70 percent, more specifically at least 90 percent.

Illustrative commercially available hydrogenated block copolymers include the polystyrene-poly(ethylene-propylene) diblock copolymers available from Kraton Performance Polymers Inc. as KRATON™ G1701 and G1702; the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymers available from Kraton Performance Polymers Inc. as KRATON™ G1641, G1650, G1651, G1654, G1657, G1726, G4609, G4610, GRP-6598, MD-6932M, MD-6933, and MD-6939; the polystyrene-poly(ethylene-propylene)-polystyrene triblock copolymers available from Kraton Performance Polymers Inc. as KRATON™ G1730; the maleic anhydride-grafted polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymers available from Kraton Performance Polymers Inc. as KRATON™ G1901, G1924, and MD-6684; the maleic anhydride-grafted polystyrene-poly(ethylene-butylene-styrene)-polystyrene triblock copolymer available from Kraton Performance Polymers Inc. as KRATON™ MD-6670; the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer comprising 67 weight percent polystyrene available from Asahi Kasei Elastomer as TUFTEC™ H1043; the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer comprising 42 weight percent polystyrene available from Asahi Kasei Elastomer as TUFTEC™ H1051; the polystyrene-poly(butadiene-butylene)-polystyrene triblock copolymers available from Asahi Kasei Elastomer as TUFTEC™ P1000 and P2000; the polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer comprising 60 weight polystyrene available from Kuraray as SEPTON™ S8104; the polystyrene-poly(ethylene-ethylene/propylene)-polystyrene triblock copolymers available from Kuraray as SEPTON™ S4044, S4055, S4077, and S4099; and the polystyrene-poly(ethylene-propylene)-polystyrene triblock copolymer comprising 65 weight percent polystyrene available from Kuraray as SEPTON™ S2104.

In some embodiments, the impact modifier is a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer having a polystyrene content of 25 to 35 weight percent and a weight average molecular weight of 200,000 to 400,000 atomic mass units.

When present, the impact modifier can be used in an amount of 2 to 10 weight percent, specifically 3 to 6 weight percent, based on the total weight of the composition.

The composition can, optionally, further comprise a hydrocarbon resin. Examples of hydrocarbon resins are aliphatic hydrocarbon resins, hydrogenated aliphatic hydrocarbon resins, aliphatic/aromatic hydrocarbon resins, hydrogenated aliphatic/aromatic hydrocarbon resins, cycloaliphatic hydrocarbon resins, hydrogenated cycloaliphatic resins, cycloaliphatic/aromatic hydrocarbon resins, hydrogenated cycloaliphatic/aromatic hydrocarbon resins, hydrogenated aromatic hydrocarbon resins, terpene resins, hydrogenated terpene resins, terpene-phenol resins, rosins, and rosin esters, hydrogenated rosins and rosin esters, and mixtures thereof. As used herein, “hydrogenated”, when referring to the hydrocarbon resin, includes fully, substantially, and partially hydrogenated resins. Suitable aromatic resins include aromatic modified aliphatic resins, aromatic modified cycloaliphatic resins, and hydrogenated aromatic hydrocarbon resins having an aromatic content of 1 to 30 weight percent. Any of the above resins can be grafted with an unsaturated ester or anhydride using methods known in the art. Such grafting can provide enhanced properties to the resin. In some embodiments, the hydrocarbon resin is a hydrogenated aromatic hydrocarbon resin.

Suitable hydrocarbon resins are commercially available and include, for example, EMPR™ 100, 101, 102, 103, 104, 105, 106, 107, 108, 109, 110, 116, 117, and 118 resins, and OPPERA™ resins, available from ExxonMobil Chemical Company; ARKON™ P140, P125, P115, M115, and M135, and SUPER ESTER™ rosin esters available from Arakawa Chemical Company of Japan; SYLVARES™ polyterpene resins, styrenated terpene resins and terpene phenolic resins available from Arizona Chemical Company; SYLVATAC™ and SYLVALITE™ rosin esters available from Arizona Chemical Company; NORSOLENE™ aliphatic aromatic resins available from Cray Valley; DERTOPHENE™ terpene phenolic resins and DERCOLYTE™ polyterpene resins available from DRT Chemical Company; EASTOTAC™ resins, PICCOTAC™ resins, REGALITE™ and REGALREZ™ hydrogenated cycloaliphatic/aromatic resins, and PICCOLYTE™ and PERMALYN™ polyterpene resins, rosins, and rosin esters available from Eastman Chemical Company; WINGTACK™ resins available from Goodyear Chemical Company; coumarone/indene resins available from Neville Chemical Company; QUINTONE™ acid modified C5 resins, C5/C9 resins, and acid-modified C5/C9 resins available from Nippon Zeon; and CLEARON™ hydrogenated terpene resins available from Yasuhara. In some embodiments, the hydrocarbon resin is a hydrogenated terpene resin. In some embodiments, the hydrocarbon resin is a saturated polyalicyclic hydrocarbon resin.

The hydrocarbon resin can have a softening point of at least 120° C. measured according to ASTM E28. Specifically, the softening point can be 120 to 180° C., specifically 130 to 170° C., more specifically 140 to 160° C. In some embodiments, the hydrocarbon resin comprises a hydrogenated alicyclic hydrocarbon resin, a hydrogenated terpene resin, or a combination thereof. In some embodiments, the hydrocarbon resin comprises a hydrogenated alicyclic hydrocarbon resin having a softening point of 120 to 135° C. An example of such a resin is ARKON™ P125 having a softening point of about 125° C., available from Arakawa Chemical Company. In some embodiments, the hydrocarbon resin comprises a hydrogenated alicyclic hydrocarbon resin having a softening point of 135 to 145° C. An example of such a resin is ARKON™ P140 having a softening point of about 140° C., available from Arakawa Chemical Company. In some embodiments, the hydrocarbon resin comprises a hydrogenated terpene resin having a softening point of 145 to 160° C. An example of such a resin is CLEARON™ P150 available from Yasuhara.

When present, the hydrocarbon resin can be used in an amount of 1 to 8 weight percent, specifically 2 to 6 weight percent, based on the total weight of the composition.

The composition can, optionally, further comprise a trihydrocarbyl phosphite. Trihydrocarbyl phosphites have the general structure P(OR¹⁸)₃, wherein each occurrence of R¹⁸ is independently C₁-C₁₈ hydrocarbyl. In some embodiments, each R¹⁸ is independently C₆-C₁₈ alkyl. In other embodiments, at least one R¹⁸ is C₆-C₁₈ aryl. In some embodiments, each occurrence of R¹⁸ is independently an unsubstituted or substituted C₆-C₁₈ aryl. Suitable trihydrocarbyl phosphites include, for example, trioctyl phosphite, tridecyl phosphite, tridodecyl phosphite, phenyl didecyl phosphite, decyl diphenyl phosphite, triphenyl phosphite, tritolyl phosphites, tris(2,4-di-tert-butylphenyl)phosphite, bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, and the like, and combinations thereof. Suitable trihydrocarbyl phosphites further include spiro diphosphites such as, for example, 3,9-bis[2,4-bis(1,1-dimethylethyl)phenoxy]-2,4,8,10-tetraoxa-3,9-diphosphaspiro[5.5]undecane (CAS Reg. No. 26741-53-7; commercially available from Ciba under the trade name IRGAFOS™ 126). In some embodiments, the aryl phosphite comprises tris(2,4-di-tert-butylphenyl)phosphite (CAS Reg. No. 31570-04-4). In some embodiments, the aryl phosphite comprises bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite (CAS Reg. No. 26741-53-7).

When present, the trihydrocarbyl phosphite can be used in an amount of 0.05 to 1 weight percent, specifically 0.1 to 0.5 weight percent, based on the total weight of the composition.

The composition can, optionally, further comprise linear low density polyethylene (LLDPE). Linear low density polyethylene is a copolymer of ethylene and a longer chain olefin such as 1-butene, 1-hexene, or 1-octene. In some embodiments, the linear low density polyethylene is a copolymer of ethylene and 1-butene. Linear low density polyethylene typically has a density of about 0.92 grams/centimeter³. When present, the linear low density polyethylene can be used in an amount of 0.5 to 5 weight percent, specifically 1 to 3 weight percent, based on the total weight of the composition.

The composition can, optionally, further comprise one or more additives known in the thermoplastics art. For example, the composition can, optionally, further comprise an additive chosen from stabilizers, mold release agents, lubricants, processing aids, drip retardants, nucleating agents, UV blockers, dyes, pigments, antioxidants, anti-static agents, blowing agents, mineral oil, metal deactivators, antiblocking agents, and the like, and combinations thereof. When present, such additives are typically used in a total amount of less than or equal to 5 weight percent, specifically less than or equal to 4 weight percent, more specifically less than or equal to 3 weight percent, based on the total weight of the composition.

The composition can, optionally, exclude polymers other than those required. For example, the composition can comprise less than or equal to 1 weight percent of each of polyamides and polyesters. In some embodiments, the composition comprises less than or equal to 4 weight percent, specifically less than or equal to 3 weight percent, more specifically less than or equal to 2 weight percent, of polyolefins. In some embodiments, the composition comprises less than or equal to 1 weight percent of polyolefins other than linear low density polyethylene. In other embodiments, the composition comprises less than or equal to 1 weight percent of any polyolefins.

One advantage of the composition is that it can achieve a UL 94 V-0 rating without using the halogenated flame retardants that are typically employed in glass-filled polyester compositions utilized for similar product applications. Thus, the composition can comprise less than or equal to 0.1 weight percent halogens, specifically less than or equal to 0.01 weight percent halogens, based on the total weight of the composition. In some embodiments, composition is halogen-free.

In a very specific embodiment of the composition, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 64 to 74 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the flame retardant comprises (or consists of) of an organophosphate ester; the composition comprises 4 to 10 weight percent of the flame retardant; the reinforcing filler comprises (or consists of) glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 2 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the composition, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the flame retardant comprises (or consists of) an organophosphate ester; the composition comprises 15 to 25 weight percent of the flame retardant; the reinforcing filler comprises (or consists of) glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the composition, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 5 to 15 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the composition further comprises 47 to 67 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; the flame retardant comprises an organophosphate ester; the composition comprises 6 to 14 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the composition, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 0.5 to 5 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the composition further comprises 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; the flame retardant comprises the organophosphate ester; the composition comprises 6 to 14 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the composition, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 0.5 to 5 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the composition further comprises 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; the flame retardant comprises the organophosphate ester; the composition comprises 6 to 14 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the composition, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the flame retardant comprises the organophosphate ester; the composition comprises 15 to 25 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters, and less than or equal to 3 weight percent of polyolefins.

The composition is useful for molding articles. Thus, one embodiment is an article comprising a composition, comprising: 0.5 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; and 5 to 40 weight percent of a reinforcing filler; wherein all weight percents are based on the total weight of the composition. The composition is particularly useful for molding articles including electrophotographic copier parts such as fuser holders, and parts for electrical components, such as photovoltaic junction boxes and connectors, inverter housings, automotive electrical connectors, electrical relays, and charge couplers. Other than their being fabricated with the present composition, such articles are known, as are methods for their fabrication. For example, U.S. Pat. No. 5,499,087 of Hiraoka et al. describes a fuser holder for an electrophotographic copier. Suitable methods of forming such articles include single layer and multilayer sheet extrusion, injection molding, blow molding, film extrusion, profile extrusion, pultrusion, compression molding, thermoforming, pressure forming, hydroforming, vacuum forming, and the like. Combinations of the foregoing article fabrication methods can be used. In some embodiments, the article is formed by injection molding.

The compositional variations described above apply as well to articles comprising the composition.

In a very specific embodiment of the article, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 64 to 74 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the flame retardant comprises an organophosphate ester; the composition comprises 4 to 10 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 2 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the article, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the flame retardant comprises an organophosphate ester; the composition comprises 15 to 25 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the article, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 5 to 15 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the composition further comprises 47 to 67 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; the flame retardant comprises an organophosphate ester; the composition comprises 6 to 14 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the article, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 0.5 to 5 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the composition further comprises 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; the flame retardant comprises the organophosphate ester; the composition comprises 6 to 14 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

In another very specific embodiment of the article, the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; the flame retardant comprises the organophosphate ester; the composition comprises 15 to 25 weight percent of the flame retardant; the reinforcing filler comprises glass fibers; the composition comprises 15 to 25 weight percent of the reinforcing filler; and the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters, and less than or equal to 3 weight percent of polyolefins.

The invention includes at least the following embodiments.

Embodiment 1: A composition, comprising: 0.5 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; and 5 to 40 weight percent of a reinforcing filler; wherein all weight percents are based on the total weight of the composition.

Embodiment 2: The composition of embodiment 1, exhibiting a flammability rating of V-0 at a sample thickness less than or equal to 1.5 millimeters in the 20 millimeter Vertical Burning Flame Test of Underwriter's Laboratory Bulletin 94 “Tests for Flammability of Plastic Materials, UL 94”, a heat deflection temperature of at least 110° C. determined according to ASTM D 648-07 using a stress of 1.82 megapascals (MPa) and a sample thickness of 6.4 millimeters, and a flexural modulus of at least 3,500 megapascals measured at 23° C. according to ASTM D 790-07e1 using a sample thickness of 6.4 millimeters.

Embodiment 3: The composition of embodiment 1 or 2, further comprising 5 to 90.5 weight percent of a second poly(phenylene ether).

Embodiment 4: The composition of embodiment 3, comprising 0.5 to 5 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product, and 30 to 90.5 weight percent of the second poly(phenylene ether).

Embodiment 5: The composition of any of embodiments 1-4, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60.

Embodiment 6: The composition of any of embodiments 1-5, wherein the poly(phenylene ether)-polysiloxane block copolymer contributes 0.025 to 5 weight percent of polysiloxane to the composition.

Embodiment 7: The composition of any of embodiments 1-6, wherein the flame retardant comprises an organophosphate ester.

Embodiment 8: The composition of any of embodiments 1-7, wherein the flame retardant comprises a phosphazene.

Embodiment 9: The composition of any of embodiments 1-8, wherein the reinforcing filler is selected from the group consisting of glass fibers, carbon fibers, wollastonite, halloysite, clays, talcs, micas, glass flakes, solid glass beads, hollow glass beads, solid ceramic beads, hollow ceramic beads, and combinations thereof.

Embodiment 10: The composition of any of embodiments 1-9, wherein the reinforcing filler comprises glass fibers.

Embodiment 11: The composition of any of embodiments 1-10, further comprising 2 to 10 weight percent of an impact modifier selected from the group consisting of rubber-modified polystyrenes, unhydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, hydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, acrylate core-shell impact modifiers, and combinations thereof.

Embodiment 12: The composition of any of embodiments 1-11, further comprising 1 to 8 weight percent of a hydrocarbon resin.

Embodiment 13: The composition of any of embodiments 1-12, further comprising 0.05 to 1 weight percent of a trihydrocarbyl phosphite.

Embodiment 14: The composition of any of embodiments 1-13, further comprising 0.5 to 5 weight percent of linear low density polyethylene.

Embodiment 15: The composition of any of embodiments 1-14, comprising less than or equal to 1 weight percent of each of polyamides and polyesters.

Embodiment 16: A composition, comprising: 0.5 to 5 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; 6 to 14 weight percent of a flame retardant comprising an organophosphate ester; 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and 15 to 25 weight percent of glass fibers; wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters; and wherein all weight percents are based on the total weight of the composition.

Embodiment 16a: The composition of embodiment 1, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 0.5 to 5 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; wherein the composition further comprises 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; wherein the flame retardant comprises the organophosphate ester; wherein the composition comprises 6 to 14 weight percent of the flame retardant; wherein the reinforcing filler comprises glass fibers; wherein the composition comprises 15 to 25 weight percent of the reinforcing filler; wherein the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

Embodiment 17: The composition of claim 1, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; wherein the flame retardant comprises the organophosphate ester; wherein the composition comprises 15 to 25 weight percent of the flame retardant; wherein the reinforcing filler comprises glass fibers; wherein the composition comprises 15 to 25 weight percent of the reinforcing filler; wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters, and less than or equal to 3 weight percent of polyolefins.

Embodiment 18: An article comprising a composition, comprising: 0.5 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a first poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; and 5 to 40 weight percent of a reinforcing filler; wherein all weight percents are based on the total weight of the composition.

Embodiment 19: The article of embodiment 18, wherein the article is a fuser holder for an electrophotographic copier.

Embodiment 20: The article of embodiment 18 or 19, wherein the composition further comprises 5 to 90.5 weight percent of a second poly(phenylene ether).

Embodiment 21: The article of embodiment 18, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 0.5 to 5 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; wherein the composition further comprises 50 to 70 weight percent of a second poly(phenylene ether) comprising a homopolymer of 2,6-dimethylphenol; wherein the flame retardant comprises an organophosphate ester; wherein the composition comprises 6 to 14 weight percent of the flame retardant; wherein the reinforcing filler comprises glass fibers; wherein the composition comprises 15 to 25 weight percent of the reinforcing filler; wherein the composition further comprises 1 to 8 weight percent of a polystyrene-poly(ethylene-butylene)-polystyrene triblock copolymer; and wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.

Embodiment 22: The article of claim 18, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; wherein the flame retardant comprises the organophosphate ester; wherein the composition comprises 15 to 25 weight percent of the flame retardant; wherein the reinforcing filler comprises glass fibers; wherein the composition comprises 15 to 25 weight percent of the reinforcing filler; wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters, and less than or equal to 3 weight percent of polyolefins.

All ranges disclosed herein are inclusive of the endpoints, and the endpoints are independently combinable with each other. Each range disclosed herein constitutes a disclosure of any point or sub-range lying within the disclosed range.

The invention is further illustrated by the following non-limiting examples.

COMPARATIVE EXAMPLES 1-15

These comparative examples utilize poly(phenylene ether) homopolymer, rather than poly(phenylene ether)-polysiloxane block copolymer reaction product.

Components used to prepare the compositions are summarized in Table 1.

TABLE 1 Component Description PPE 0.46 Poly(2,6-dimethyl-1,4-phenylene ether), CAS Reg. No. 25134-01-4, having an intrinsic viscosity of about 0.46 deciliter per gram measured in chloroform at 25° C.; available as PPO ™ 646 from SABIC Innovative Plastics. PPE 0.40 Poly(2,6-dimethyl-1,4-phenylene ether), CAS Reg. No. 25134-01-4, having an intrinsic viscosity of about 0.40 deciliter per gram measured in chloroform at 25° C.; available as PPO ™ 640 from SABIC Innovative Plastics. PPE 0.33 Poly(2,6-dimethyl-1,4-phenylene ether), CAS Reg. No. 25134-01-4, having an intrinsic viscosity of about 0.33 deciliter per gram measured in chloroform at 25° C.; available as PPO ™ 630 from SABIC Innovative Plastics. PPE 0.30 Poly(2,6-dimethyl-1,4-phenylene ether), CAS Reg. No. 25134-01-4, having an intrinsic viscosity of about 0.30 deciliter per gram measured in chloroform at 25° C.; available as PPO ™ 808 from SABIC Innovative Plastics. PPE-Si A mixture of poly(2,6-dimethyl-1,4-phenylene ether) (CAS Reg. No. 24938-67-8) and poly(2,6-dimethyl-1,4-phenylene ether)- polydimethylsiloxane block copolymer (CAS Reg. No. 1202019-56-4), the mixture having a polysiloxane content of about 5 weight percent and an intrinsic viscosity of about 0.4 deciliter per gram as measured in chloroform at 25° C.; prepared according to the procedure of U.S. Patent No. 8,017,697 to Carrillo et al., Example 16. SEBS Polystyrene-poly(ethylene/butylene)-polystyrene triblock copolymer, CAS Reg. No. 66070-58-4, having a polystyrene content of 30-33 weight percent and a weight average molecular weight of 240,000-301,000 atomic mass units; obtained as KRATON ™ G1651 from Kraton Performance Polymers Inc. AO 168 Tris(2,4-di-tert-butylphenyl) phosphite, CAS Reg. No. 31570-04-4, available from BASF Corp. as IRGAFOS ™ 168, or from Chemtura as ALKANOX ™ 240. AO 626 Bis(2,4-di-tert-butylphenyl)pentaerythritol diphosphite, CAS Reg. No. 26741-53-7, available from Chemtura as ULTRANOX ™ 626 HCR Saturated polyalicyclic hydrocarbon resin, CAS Reg. No. 64742-16-1, available from Arakawa Chemical as ARKON ™ P-125. HIPS Rubber-modified polystyrene, CAS Reg. No. 9003-55-8, available from SABIC Innovative Plastics as HIPS3190. Clay Water-washed kaolin clay, CAS Reg. No. 1332-58-7, available as KaMin POLYFIL ™ HG90 from KaMin Performance Minerals. Mica Phlogopite mica, CAS Reg. No. 12001-26-2, available from Imerys Performance Minerals as SUZORITE ™ HK-200. Glass Fiber Chopped glass fiber having a diameter of about 14 micrometers and a pre- compounded length of about 4 millimeters; available from Owens Corning as 122Y-14C. Carbon Carbon black pigment, CAS Reg. No. 1333-86-4, available from Cabot as Black BLACK PEARLS ™ 800 or MONARCH ™ 800. LLDPE Linear low density polyethylene (copolymer of ethylene and 1-butene), CAS Reg. No. 25087-34-7, having a density of 0.925 grams per cubic centimeter and a melt volume flow rate of 20 cubic centimeters per 10 minutes at 190° C. and 2.16 kilogram load, available from ExxonMobil as ESCORENE ™ LL5100.09. MgO Magnesium oxide, CAS Reg. No. 1309-48-4, available from Kyowa Chemical Co. Ltd. as KYOWAMAG ™ 150. ZnS Zinc sulfide, CAS Reg. No. 1314-98-3, available from Sachtleben Chemie GmbH as SACHTOLITH ™ HD-S. But-TPP t-Butylated triphenyl phosphate, CAS Reg. No. 220352-35-2, available as PHOSFLEX ™ 71B from Supresta LLC. BPADP Bisphenol A bis(diphenyl phosphate), CAS Reg. No. 181028-79-5; obtained as FYROFLEX ™ BDP from Supresta LLC, or REOFOS ™ BAPP from Great Lakes Chemical Co. Ltd.

Resin compositions were compounded on a 30 millimeter Werner & Pfleiderer ZSK twin-screw extruder operating at 350 rotations per minute and a throughput of 18 kilograms per hour (40 pounds per hour) and using barrel set temperatures of 240° C./260° C./290° C./290° C./290° C. from the feed port to die. Glass fibers were added downstream to the extruder, while all other solid components were added at the feed throat and the liquid flame retardant (But-TPP or BPADP) was injected at a port between the feed throat and the glass fiber feed location. The compounded resins were pelletized by strand-cutting.

Test articles for ASTM determinations of heat deflection temperature and flexural properties were injection molded on a 120 Ton VanDorn injection molding machine using a barrel temperature of 288-310° C. (550-590° F.) and a mold temperature of about 88° C. (about 190° F.). Flame bars with 1.0 or 1.5 millimeter thickness were injection molded on an 80 Ton VanDorn injection molding machine using a barrel temperature of 299-321° C. (570-610° F.) and a mold temperature of 88-99° C. (190-210° F.).

Flame retardancy of injection molded flame bars was determined according to Underwriter's Laboratory Bulletin 94 “Tests for Flammability of Plastic Materials, UL 94”, 20 mm Vertical Burning Flame Test. Before testing, flame bars with a thickness of 1.0 or 1.5 millimeters were conditioned at 23° C. and 50% relative humidity for at least 24 hours. In the UL 94 20 mm Vertical Burning Flame Test, a set of ten flame bars was tested. For each bar, a flame was applied to the bar then removed, and the time required for the bar to self-extinguish (first afterflame time, t1) was noted. The flame was then reapplied and removed, and the time required for the bar to self-extinguish (second afterflame time, t2) and the post-flame glowing time (afterglow time, t3) were noted. To achieve a rating of V-0, the afterflame times t1 and t2 for each individual specimen must have been less than or equal to 10 seconds; and the total afterflame time for all ten specimens (t1 plus t2 for all ten specimens) must have been less than or equal to 100 seconds; and the second afterflame time plus the afterglow time for each individual specimen (t2+t3) must have been less than or equal to 30 seconds; and no specimen can have flamed or glowed up to the holding clamp; and the cotton indicator cannot have been ignited by flaming particles or drops. To achieve a rating of V-1, the afterflame times t1 and t2 for each individual specimen must have been less than or equal to 30 seconds; and the total afterflame time for all ten specimens (t1 plus t2 for all ten specimens) must have been less than or equal to 500 seconds; and the second afterflame time plus the afterglow time for each individual specimen (t2+t3) must have been less than or equal to 60 seconds; and no specimen can have flamed or glowed up to the holding clamp; and the cotton indicator cannot have been ignited by flaming particles or drops. To achieve a rating of V-2, the afterflame times t1 and t2 for each individual specimen must have been less than or equal to 30 seconds; and the total afterflame time for all ten specimens (t1 plus t2 for all ten specimens) must have been less than or equal to 250 seconds; and the second afterflame time plus the afterglow time for each individual specimen (t2+t3) must have been less than or equal to 60 seconds; and no specimen can have flamed or glowed up to the holding clamp; but the cotton indicator can have been ignited by flaming particles or drops. Compositions not achieving a rating of V-2 were considered to have failed.

Heat deflection temperature (HDT) values, expressed in units of degrees centigrade, were determined according to ASTM D 648-07 using 6.4 millimeter thick bars (except where specified as 3.2 millimeter thickness), an edgewise test direction, a support span of 100 millimeters (Method B), a stress of 1.82 megapascals, a deflection of 0.25 millimeters at reading, a heating rate of 2° C./minute, and three specimens per composition. Flexural modulus and flexural stress at break values, each in units of megapascals, were determined at 23° C. according to ASTM D 790-07e1 using 6.4 millimeter thick bars, a support span of 101.6 millimeters, a test speed of 2.54 millimeters/minute (0.1 inch/minute; Procedure A), and three specimens per composition.

Compositions and results are summarized in Table 2, where component amounts are expressed in weight percent based on the total weight of the composition.

The Table 2 results show that the achievement of a flame retardancy rating of V-0 at a bar thickness of 1.5 millimeters is limited to Comparative Examples 1-3 with very high flame retardant concentrations (≧21.00 weight percent) and correspondingly low heat deflection temperatures (≦112° C.). A flame retardancy rating of V-0 at 1.0 millimeter thickness was only observed for Comparative Example 1 with a low heat deflection temperature of 106° C.

TABLE 2 C. Ex. 1 C. Ex. 2 C. Ex. 3 C. Ex. 4 C. Ex. 5 COMPOSITIONS PPE 0.40 63 56 49 67.5 60 BPADP 27 24 21 22.5 20 Glass fiber 10 20 30 10 20 PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 Fail Fail UL 94 rating at 1.0 mm V-0 V-1 V-1 V-1 V-1 HDT (° C.) 106 111 112 120 124 Flex. modulus (MPa) 4670 7120 9610 4670 6850 Flex. stress at break (MPa) 144 153 159 145 149 C. Ex. 6 C. Ex. 7 C. Ex. 8 C. Ex. 9 C. Ex. 10 COMPOSITIONS PPE 0.40 52.5 72 64 56 76.5 BPADP 17.5 18 16 14 13.5 Glass fiber 30 10 20 30 10 PROPERTIES UL 94 rating at 1.5 mm V-1 V-1 V-1 V-1 V-1 UL 94 rating at 1.0 mm V-1 V-1 V-1 V-1 V-1 HDT (° C.) 124 133 137 138 149 Flex. modulus (MPa) 9090 4370 6490 8380 4250 Flex. stress at break (MPa) 158 147 149 151 145 C. Ex. 11 C. Ex. 12 C. Ex. 13 C. Ex. 14 C. Ex. 15 COMPOSITIONS PPE 0.40 68 59.5 81 72 63 BPADP 12 10.5 9 8 7 Glass fiber 20 30 10 20 30 PROPERTIES UL 94 rating at 1.5 mm Fail V-1 V-1 V-1 V-1 UL 94 rating at 1.0 mm V-1 Fail V-1 V-1 V-1 HDT (° C.) 152 154 164 168 170 Flex. modulus (MPa) 6000 8050 4100 5830 7890 Flex. stress at break (MPa) 142 152 142 145 155

COMPARATIVE EXAMPLES 16-23

Eight comparative examples were prepared using poly(phenylene ether) homopolymer and the hydrogenated block copolymer SEBS. These examples illustrate that it is not feasible to achieve a V-0 rating at 1.5 millimeter thickness in a composition with a heat deflection temperature of at least 150° C. and at least 10% glass fiber reinforcement, even though the corresponding unfilled compositions (Comparative Examples 16 and 20) have a V-0 flame retardancy. Relative to the property balance exhibited by the inventive composition, unfilled Comparative Examples 16 and 20 are deficient in flexural modulus, and filled Comparative Examples 17-19 and 21-23 are deficient in UL 94 rating, at least

TABLE 3 C. Ex. 16 C. Ex. 17 C. Ex. 18 C. Ex. 19 C. Ex. 20 COMPOSITIONS PPE 0.46 84.70 76.23 67.76 72.00 82.70 BPADP 10.00 9.00 8.00 8.50 12.00 SEBS 5.00 4.5 4.00 4.25 5.00 AO 168 0.30 0.27 0.24 0.25 0.30 Glass fiber 0.00 10 20 10.00 0.00 Clay 0.00 0.00 0.00 5.00 0.00 PROPERTIES UL 94 rating at 1.5 mm V-0 V-1 V-1 V-1 V-0 HDT (° C.) 146 159 163 159 139 Flex. modulus (MPa) 2520 3721 5234 4235 2570 Flex. stress at break (MPa) 106 122 132 136 108 C. Ex. 21 C. Ex. 22 C. Ex. 23 COMPOSITIONS PPE 0.46 74.43 66.16 70.30 BPADP 10.80 9.60 10.20 SEBS 4.50 4.00 4.25 AO 168 0.27 0.24 0.25 Glass fiber 10.00 20.00 10.00 Clay 0.00 0.00 5.00 PROPERTIES UL 94 rating at 1.5 mm V-1 V-1 V-1 HDT (° C.) 152 156 153 Flex. modulus (MPa) 3937 5363 4297 Flex. stress at break (MPa) 128 131 135

EXAMPLES 1-6, COMPARATIVE EXAMPLES 24 AND 25

These inventive and comparative examples illustrate the use of a poly(phenylene ether)-polysiloxane block copolymer in combination with the hydrogenated block copolymer SEBS. Inventive Examples 1-6 all have heat deflection temperature values of at least 155° C., as well as UL 94 ratings of V-0 at 1.5 millimeter thickness, and flexural modulus values greater than 3,500 megapascals. Comparative Examples 24 and 25 are unfilled and exhibit substantially lower heat deflection temperature values, flexural modulus values, and flexural strength values.

TABLE 4 C. Ex. 24 Ex. 1 Ex. 2 Ex. 3 C. Ex. 25 COMPOSITIONS PPE-Si 87.70 78.93 70.16 74.55 85.70 BPADP 7.00 6.30 5.60 5.95 9.00 SEBS 5.00 4.50 4.00 4.25 5.00 AO 168 0.30 0.27 0.24 0.25 0.30 Glass fiber 0.00 10.00 20.00 10.00 0.00 Clay 0.00 0.00 0.00 5.00 0.00 PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 V-0 V-0 HDT (° C.) 149 163 168 163 140 Flex. modulus (MPa) 2310 3506 4942 3891 2350 Flex. stress at break (MPa) 94 119 133 125 96 Ex. 4 Ex. 5 Ex. 6 COMPOSITIONS PPE-Si 77.13 68.56 72.85 BPADP 8.10 7.20 7.65 SEBS 4.50 4.00 4.25 AO 168 0.27 0.24 0.25 Glass fiber 10.00 20.00 10.00 Clay 0.00 0.00 5.00 PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 HDT (° C.) 155 160 158 Flex. modulus (MPa) 3739 5027 4039 Flex. stress at break (MPa) 123 130 129

EXAMPLES 7-15, COMPARATIVE EXAMPLE 26

These inventive and comparative examples illustrate means of achieving improved melt flow.

Melt volume flow rate (MVR) values, expressed in units of cubic centimeters per 10 minutes, were determined according to ASTM D 1238-04 at 300° C. using a load of 5 kilograms, automatic timing (Procedure B), a capillary diameter of 2.0955 millimeters, a capillary length of 8.00 millimeters, a test specimen form of pellets, specimen conditioning for one hour at 70° C. prior to testing, and one sample with five readings per composition.

The results in Table 5 show that the inventive compositions can be modified to increase melt flow while still maintaining a high heat deflection temperature and a UL 94 rating of V-0 at 1.5 millimeters. Inventive Example 13 shows that a reduced concentration of poly(phenylene ether)-polysiloxane block copolymer also still results in V-0 at 1.5 mm. Inventive Example 15 illustrates the use of a mixed filler reinforcement. The examples also show that melt flow increases can be accomplished through use of a hydrocarbon resin flow promoter (Examples 10-15) and/or a phosphite antioxidant like AO 626. Inventive Example 7, without either hydrocarbon resin or phosphite antioxidant, exhibits relatively lower melt flow. Comparative Example 26 shows again that with poly(phenylene ether) homopolymer rather than poly(phenylene ether)-polysiloxane block copolymer reaction product, even a higher concentration of flame retardant does not result in V-0 flammability rating at 1.5 millimeters.

TABLE 5 Ex. 7 Ex. 8 Ex. 9 Ex. 10 Ex. 11 COMPOSITIONS PPE-Si 68.66 68.26 67.86 68.26 68.26 PPE 0.40 0.00 0.00 0.00 0.00 0.00 BPADP 6.97 6.97 6.97 6.97 6.97 SEBS 3.98 3.98 3.98 1.99 0.00 HCR 0.00 0.00 0.00 1.99 3.98 AO 626 0.00 0.40 0.80 0.40 0.40 Carbon black 0.50 0.50 0.50 0.50 0.50 Glass fiber 19.90 19.90 19.90 19.90 19.90 Mica 0.00 0.00 0.00 0.00 0.00 PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 V-0 V-0 HDT (° C.) 161 158 157 156 153 MVR (cc/10 min) 2.8 8.8 12.6 11.6 14.1 Flex. modulus (MPa) 5150 5180 5310 5320 5500 Flex. stress at break 137 136 131 131 138 (MPa) Ex. 12 Ex. 13 Ex. 14 Ex. 15 C. Ex. 26 COMPOSITIONS PPE-Si 67.86 33.43 77.21 72.74 0.00 PPE 0.40 0.00 33.43 0.00 0.00 65.27 BPADP 6.97 8.36 7.96 7.46 9.95 SEBS 0.00 1.99 1.99 1.99 3.98 HCR 3.98 1.99 1.99 1.99 0.00 AO 626 0.80 0.40 0.40 0.40 0.40 Carbon black 0.50 0.50 0.50 0.50 0.50 Glass fiber 19.90 19.90 9.95 9.95 19.90 Mica 0.00 0.00 0.00 4.98 0.00 PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 V-0 V-1 HDT (° C.) 151 153 152 153 155 MVR (cc/10 min) 21.8 13.1 16.3 13.4 8.28 Flex. modulus (MPa) 5660 5480 3910 4367 5640 Flex. stress at break 134 133 122 124 136 (MPa)

EXAMPLES 16-19

These inventive examples illustrate that omission of hydrogenated block copolymer is associated with even higher heat deflection temperature values.

TABLE 6 Ex. 16 Ex. 17 Ex. 18 Ex. 19 COMPOSITIONS PPE-Si 76.32 71.84 67.86 73.83 BPADP 7.46 6.97 6.97 4.98 HCR 0.00 0.00 3.98 0.00 AO 626 0.80 0.80 0.80 0.80 Carbon black 0.50 0.50 0.50 0.50 Glass fiber 9.95 19.90 19.90 19.90 Mica 4.98 0.00 0.00 0.00 PROPERTIES UL 94 rating at 1.5 mm V-0 V-0 V-0 V-0 HDT (° C.) 157 159 153 168 MVR (cc/10 min) 18 14 23 9 Flex. modulus (MPa) 4700 5680 5650 5520 Flex. stress at break (MPa) 118 136 128 135

EXAMPLES 20 AND 21, COMPARATIVE EXAMPLES 27 AND 28

These inventive and comparative examples, all with 20% glass fiber reinforcement, illustrate that the improved flame retardancy associated with the use of poly(phenylene ether)-polysiloxane block copolymer reaction product rather than poly(phenylene ether) homopolymer can be obtained without sacrificing heat resistance. Comparative Example 28 also illustrates that a reduction of HIPS concentration and increases in flame retardant and poly(phenylene ether) homopolymer, all relative to Comparative Example 27, are not sufficient to result in V-0 flame performance at 1.5 millimeters.

TABLE 7 C. Ex. 27 Ex. 20 C. Ex. 28 Ex. 21 COMPOSITIONS PPE 0.46 48.00 0.00 55.00 0.00 PPE-Si 0.00 52.00 0.00 59.00 HIPS 24.50 20.50 16.50 12.50 But-TPP 6.00 6.00 7.00 7.00 LLDPE 1.00 1.00 1.00 1.00 AO 626 0.30 0.30 0.30 0.30 ZnS 0.10 0.10 0.10 0.10 MgO 0.10 0.10 0.10 0.10 Glass fiber 20.00 20.00 20.00 20.00 PROPERTIES UL 94 rating at 1.5 mm V-1 V-0 V-1 V-0 HDT at 3.2 mm (° C.) 132 132 135 137

EXAMPLES 22 And 23, COMPARATIVE EXAMPLES 29 And 30

These inventive and comparative examples, all with 30% glass fiber reinforcement, further illustrate that the improved flame retardancy associated with the use of poly(phenylene ether)-polysiloxane block copolymer reaction product rather than poly(phenylene ether) homopolymer can be obtained without substantially sacrificing heat resistance. Comparative Example 30 also illustrates that a reduction of HIPS concentration and increases in flame retardant and poly(phenylene ether) homopolymer, all relative to Comparative Example 29, are not sufficient to result in V-0 flame performance at 1.5 millimeters.

TABLE 8 C. Ex. 29 Ex. 22 C. Ex. 30 Ex. 23 COMPOSITIONS PPE 0.46 49.00 0.00 51.50 0.00 PPE-Si 0.00 53.00 0.00 56.00 HIPS 12.00 8.00 8.50 4.00 But-TPP 7.50 7.50 8.50 8.50 LLDPE 1.00 1.00 1.00 1.00 AO 168 0.30 0.30 0.30 0.30 ZnS 0.10 0.10 0.10 0.10 MgO 0.10 0.10 0.10 0.10 Glass fiber 30.00 30.00 30.00 30.00 PROPERTIES UL 94 rating at 1.5 mm V-1 V-0 V-1 V-0 HDT at 3.2 mm (° C.) 136 135 135 136

EXAMPLES 24-26, COMPARATIVE EXAMPLES 31-36

These inventive and comparative examples demonstrate that it is also possible to achieve a UL 94 rating of V-0 at a thickness of 0.75 millimeters in a 20% glass fiber reinforced composition containing poly(phenylene ether)-polysiloxane block copolymer, while maintaining a heat deflection temperature greater than 110° C. Comparative Example 36 achieved a V-0 rating but was deficient in heat deflection temperature.

TABLE 9 Ex. 24 Ex. 25 Ex. 26 C. Ex. 31 C. Ex. 32 COMPOSITIONS PPE-Si 57.81 59.80 61.79 0.00 0.00 PPE 0.40 0.00 0.00 0.00 57.81 54.83 PPE 0.46 0.00 0.00 0.00 0.00 0.00 BPADP 19.90 17.91 15.92 19.90 22.89 Glass fiber 19.90 19.90 19.90 19.90 19.90 LLDPE 1.49 1.49 1.49 1.49 1.49 AO 168 0.10 0.10 0.10 0.10 0.10 ZnS 0.15 0.15 0.15 0.15 0.15 MgO 0.15 0.15 0.15 0.15 0.15 Carbon black 0.50 0.50 0.50 0.50 0.50 PROPERTIES UL 94 rating at 0.75 mm V-0 V-0 V-0 V-1 V-1 HDT (° C.) 113 121 128 119 109 Flex. modulus (MPa) 6094 6178 6104 6530 6570 Flex. stress at break (MPa) 155 158 158 160 155 C. Ex. 33 C. Ex. 34 C. Ex. 35 C. Ex. 36 COMPOSITIONS PPE-Si 0.00 0.00 0.00 0.00 PPE 0.40 51.84 0.00 0.00 0.00 PPE 0.46 0.00 57.81 54.83 51.84 BPADP 25.87 19.90 22.89 25.87 Glass fiber 19.90 19.90 19.90 19.90 LLDPE 1.49 1.49 1.49 1.49 AO 168 0.10 0.10 0.10 0.10 ZnS 0.15 0.15 0.15 0.15 MgO 0.15 0.15 0.15 0.15 Carbon black 0.50 0.50 0.50 0.50 PROPERTIES UL 94 rating at 0.75 mm V-1 V-1 V-1 V-0 HDT (° C.) 100 120 110 100 Flex. modulus (MPa) 6661 6638 6539 6717 Flex. stress at break (MPa) 145 161 153 146

EXAMPLES 27-43, COMPARATIVE EXAMPLES 37-39

These examples illustrate the attainment of a UL 94 V-0 rating at a thickness of 1.5 millimeters by compositions comprising as little as 0.5 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product. They further illustrate compositions comprising a first poly(phenylene ether) (derived from the poly(phenylene ether)-polysiloxane block copolymer reaction product) and a second poly(phenylene ether) (separately added; see Examples 28-43).

Notched Izod values and unnotched Izod values, each expressed in units of joules/meter, were determined according to ASTM D256-08 at 25° C. using a hammer energy of 2 foot-pounds (2.71 joules), and bar cross-sectional dimensions of 3.2 by 12.7 millimeters. Flexural modulus, flexural stress at yield, and flexural stress at break values, each in units of megapascals, were determined at 23° C. according to ASTM D 790-07e1 using 6.4 millimeter thick bars, a support span of 101.6 millimeters, a test speed of 2.54 millimeters/minute (0.1 inch/minute; Procedure A), and three specimens per composition. Tensile modulus and tensile stress at break values, each expressed in units of megapascals, and tensile elongation at break values, expressed in units of percent, were determined according to ASTM D 638-08 at 23° C. using a Type I bar having a thickness of 3.2 millimeters, a gage length of 50 millimeters, and a testing speed of 5 millimeters per minute.

The results demonstrate that compositions with 0.5 to 40 weight percent poly(phenylene ether)-polysiloxane block copolymer reaction product exhibit a UL 94 V-0 rating at a thickness of 1.5 millimeters. Although physical properties were not measured for all samples, the available results show that compositions with 2 to 40 weight percent poly(phenylene ether)-polysiloxane block copolymer reaction product further exhibit a heat deflection temperature of at least 150° C. determined according to ASTM D 648-07 using a stress of 1.82 megapascals (MPa) and a sample thickness of 6.4 millimeters, and a flexural modulus of at least 5,000 megapascals measured at 23° C. according to ASTM D 790-07e1 using a sample thickness of 6.4 millimeters. Comparative Examples 37 and 38, without poly(phenylene ether)-polysiloxane block copolymer, and Comparative Example 39, with only 0.4 weight percent poly(phenylene ether)-polysiloxane block copolymer, do not achieve a UL 94 V-0 rating at a thickness of 1.5 millimeters.

TABLE 10 Ex. 27 Ex. 28 Ex. 29 Ex. 30 Ex. 31 COMPOSITIONS PPE-Si 68.2 40.0 30.0 20.0 10.0 PPE 0.33 0.0 0.0 0.0 0.0 0.0 PPE 0.30 0.0 30.8 39.3 48.8 56.8 PDMS/silica 0.0 0.0 0.0 0.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR 4.0 0.0 0.0 0.0 0.0 SEBS 0.0 1.0 2.0 2.0 3.0 AO 626 0.8 0.0 0.0 0.0 0.0 AO 168 0.0 0.2 0.2 0.2 0.2 BPADP 7.0 8.0 8.5 9.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0 Polysiloxane content 3.4 2.0 1.5 1.0 0.5 PROPERTIES UL Rating at 1.5 mm V-0 V-0 V-0 V-0 V-0 UL Rating at 1.0 mm V-0 V-0 V-0 V-0 V-0 HDT (° C.) 153 159 159 157 153 Notched Izod (J/m) 69.8 87.8 95.2 90.8 96 Unnotched Izod (J/m) 338 466 478 492 457 Flex. modulus (MPa) 5460 5240 5210 5090 5180 Flex. stress at yield (MPa) 131 140 143 140 143 Flex. stress at break (MPa) 132 141 140 140 143 Tens. modulus (MPa) 6900 6818 6784 6768 6784 Tensile stress at break (MPa) 114 119 118 120 120 Tens. elong. at break (%) 2.2 2.5 2.5 2.5 2.5 C. Ex. 37 Ex. 32 Ex. 33 Ex. 34 Ex. 35 COMPOSITIONS PPE-Si 0.0 20.0 10.0 8.0 6.0 PPE 0.33 0.0 0.0 0.0 0.0 0.0 PPE 0.30 65.8 47.8 57.8 59.8 61.8 PDMS/silica 0.0 0.0 0.0 0.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR 0.0 0.0 0.0 0.0 0.0 SEBS 4.0 2.0 2.0 2.0 2.0 AO 626 0.0 0.0 0.0 0.0 0.0 AO 168 0.2 0.20 0.20 0.20 0.20 BPADP 10.0 10.0 10.0 10.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0 Polysiloxane content 0.0 1.0 0.5 0.4 0.3 PROPERTIES UL Rating at 1.5 mm V-1 V-0 V-0 V-0 V-0 UL Rating at 1.0 mm V-1 — — — — HDT (° C.) 153 153 154 155 155 Notched Izod (J/m) 101 79.8 82.0 86.6 83.3 Unnotched Izod (J/m) 515 495 516 503 511 Flex. modulus (MPa) 5270 5330 5390 5400 5400 Flex. stress at yield (MPa) 147 — — — — Flex. stress at break (MPa) 144 133 135 134 138 Tens. modulus (MPa) 6694 — — — — Tensile stress at break (MPa) 117 — — — — Tens. elong. at break (%) 2.5 — — — — Ex. 36 Ex. 37 C. Ex. 38 Ex. 38 Ex. 39 COMPOSITIONS PPE-Si 4.0 2.0 0.0 4.0 2.0 PPE 0.33 0.0 0.0 0.0 63.8 65.8 PPE 0.30 63.8 65.8 67.8 0.0 0.0 PDMS/silica 0.0 0.0 0.0 0.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR 0.0 0.0 0.0 0.0 0.0 SEBS 2.0 2.0 2.0 2.0 2.0 AO 626 0.0 0.0 0.0 0.0 0.0 AO 168 0.2 0.20 0.20 0.20 0.20 BPADP 10.0 10.0 10.0 10.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0 Polysiloxane content 0.2 0.1 0.0 0.2 0.1 PROPERTIES UL Rating at 1.5 mm V-0 V-0 V-1 V-0 V-0 UL Rating at 1.0 mm — — — — — HDT (° C.) 155 155 156 — — Notched Izod (J/m) 81.1 79.5 81.3 — — Unnotched Izod (J/m) 496 475 475 — — Flex. modulus (MPa) 5460 5490 5560 — — Flex. stress at yield (MPa) — — — — — Flex. stress at break (MPa) 133 138 135 — — Tens. modulus (MPa) — — — — — Tensile stress at break (MPa) — — — — — Tens. elong. at break (%) — — — — — Ex. 40 Ex. 41 Ex. 42 Ex. 43 C. Ex. 39 COMPOSITIONS PPE-Si 1.0 0.50 1.60 0.80 0.40 PPE 0.33 66.8 67.3 66.2 67.0 67.4 PPE 0.30 0.0 0.0 0.0 0.0 0.0 PDMS/silica 0.0 0.0 0.0 0.0 0.0 PDMS 0.0 0.0 0.0 0.0 0.0 HCR 0.0 0.0 0.0 0.0 0.0 SEBS 2.0 2.0 2.0 2.0 2.0 AO 626 0.0 0.0 0.0 0.0 0.0 AO 168 0.2 0.20 0.20 0.20 0.20 BPADP 10.0 10.0 10.0 10.0 10.0 Glass fiber 20.0 20.0 20.0 20.0 20.0 Polysiloxane content 0.05 0.025 0.08 0.04 0.02 PROPERTIES UL Rating at 1.5 mm V-0 V-0 V-0 V-0 V-1 UL Rating at 1.0 mm — — — — — HDT (° C.) — — — — — Notched Izod (J/m) — — — — — Unnotched Izod (J/m) — — — — — Flex. modulus (MPa) — — — — — Flex. stress at yield (MPa) — — — — — Flex. stress at break (MPa) — — — — — Tens. modulus (MPa) — — — — — Tensile stress at break (MPa) — — — — — Tens. elong. at break (%) — — — — — 

The invention claimed is:
 1. A composition, comprising: 30 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; 5 to 40 weight percent of a reinforcing filler; and, 3 to 6 weight percent of an impact modifier selected from the group consisting of rubber-modified polystyrenes, unhydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, hydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, acrylate core-shell impact modifiers, and combinations thereof; wherein all weight percents are based on the total weight of the composition.
 2. The composition of claim 1, exhibiting a flammability rating of V-0 at a sample thickness less than or equal to 1.5 millimeters in the 20 millimeter Vertical Burning Flame Test of Underwriter's Laboratory Bulletin 94 “Tests for Flammability of Plastic Materials, UL 94”, a heat deflection temperature of at least 110 ° C. determined according to ASTM D 648-07 using a stress of 1.82 megapascals (MPa) and a sample thickness of 6.4 millimeters, and a flexural modulus of at least 3,500 megapascals measured at 23° C. according to ASTM D 790-07e1 using a sample thickness of 6.4 millimeters.
 3. The composition of claim 1, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to
 60. 4. The composition of claim 1, wherein the poly(phenylene ether)-polysiloxane block copolymer contributes 1 to 5 weight percent of polysiloxane to the composition.
 5. The composition of claim 1, wherein the flame retardant comprises an organophosphate ester.
 6. The composition of claim 1, wherein the flame retardant comprises a phosphazene.
 7. The composition of claim 1, wherein the reinforcing filler is selected from the group consisting of glass fibers, carbon fibers, wollastonite, halloysite, clays, talcs, micas, glass flakes, solid glass beads, hollow glass beads, solid ceramic beads, hollow ceramic beads, and combinations thereof.
 8. The composition of claim 1, wherein the reinforcing filler comprises glass fibers.
 9. The composition of claim 1, wherein the reinforcing filler consists of glass fibers.
 10. The composition of claim 1, comprising the impact modifier; wherein the impact modifier is selected from the group consisting of rubber-modified polystyrenes, unhydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, acrylate core-shell impact modifiers, and combinations thereof.
 11. The composition of claim 1, further comprising 1 to 8 weight percent of a hydrocarbon resin.
 12. The composition of claim 1, further comprising 0.05 to 1 weight percent of a trihydrocarbyl phosphite.
 13. The composition of claim 1, further comprising 0.5 to 5 weight percent of linear low density polyethylene.
 14. The composition of claim 1, comprising 0 to 1 weight percent of each of polyamides and polyesters.
 15. The composition of claim 1, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; wherein the flame retardant comprises an organophosphate ester; wherein the composition comprises 15 to 25 weight percent of the flame retardant; wherein the reinforcing filler comprises glass fibers; wherein the composition comprises 15 to 25 weight percent of the reinforcing filler; and wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters.
 16. An article comprising a composition, comprising: 30 to 91 weight percent of a poly(phenylene ether)-polysiloxane block copolymer reaction product comprising a poly(phenylene ether) and a poly(phenylene ether)-polysiloxane block copolymer; 4 to 25 weight percent of a flame retardant comprising an organophosphate ester, a phosphazene, or a combination thereof; 5 to 40 weight percent of a reinforcing filler; and 3 to 6 weight percent of an impact modifier selected from the group consisting of rubber-modified polystyrenes, unhydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, hydrogenated block copolymers of an alkenyl aromatic monomer and a conjugated diene, acrylate core-shell impact modifiers, and combinations thereof; wherein all weight percents are based on the total weight of the composition.
 17. The article of claim 16, wherein the article is selected from the group consisting of electrophotographic copier parts, photovoltaic junction boxes and connectors, inverter housings, automotive electrical connectors, electrical relays, and charge couplers.
 18. The article of claim 16, wherein the article is a fuser holder for an electrophotographic copier.
 19. The article of claim 16, wherein the poly(phenylene ether)-polysiloxane block copolymer comprises a poly(phenylene ether) block comprising phenylene ether repeating units having the structure

and a polysiloxane block having the structure

wherein n is 30 to 60; wherein the composition comprises 53 to 63 weight percent of the poly(phenylene ether)-polysiloxane block copolymer reaction product; wherein the flame retardant comprises an organophosphate ester; wherein the composition comprises 15 to 25 weight percent of the flame retardant; wherein the reinforcing filler comprises glass fibers; wherein the composition comprises 15 to 25 weight percent of the reinforcing filler; and wherein the composition comprises less than or equal to 1 weight percent of each of polyamides and polyesters. 